New Method to Produce Thin Crystalline Silicon Wafers for Solar Cells

IMEC is developing a new method to produce ~50µm thin crystalline silicon wafers for use in solar cells. The process involves mechanically initiating and propagating a crack parallel to the surface of a Si wafer. In this way, Si foils with an area of 25cm² and a thickness of 30-50µm have already been produced. The method makes use of industrially available tools (screen printer, belt furnace) and is potentially kerf-loss free.

Ultra-thin crystalline Si foil; this side shows the surface cut from the thicker substrate.

Adding an ultra-thin wafer or foil of active silicon on top of a low-cost substrate is a promising solution to reduce the amount of high-grade silicon used in solar cells. IMEC is pursuing different paths to produce such foils of crystalline Si at an acceptable cost. One of the promising methods is a lift-off process that only requires the use of a screen printer and a belt furnace; no ion-implanted or porous layer is needed.

A metallic layer is screenprinted on top of a thick crystalline Si wafer, which is then annealed in a belt furnace at a high temperature. When the wafer cools, the mismatch of the thermal expansion coefficient between the metal and the silicon induces a stress field in the substrate.

The stress field grows, initiating and propagating a crack in the silicon, close to and parallel with the surface. Next, the top layer of the silicon and the attached metal layer snap off from the parent substrate. The metal layer is removed from the silicon foil in a metal-etching solution, resulting in a clean and stress-free ultra-thin silicon foil. The substrate can be re-used to peel off further layers.

The process was demonstrated on both single- and multi-crystalline silicon, as well as on Cz (Czochralski or a method of crystal growth used to obtain single crystals of semiconductors) material with different orientations.
IMEC already produced foils with an area of 25cm2 and a thickness of 30-50µm.

One of the resulting thin Cz foils was further processed into a solar cell using a heterojunction emitter process. The 1cm² cell reached an efficiency of 10.0%, without back-surface passivation or intentional surface texturing. These preliminary results indicate that the quality of the material is largely preserved during the lift-off process, in spite of the large stresses involved. IMEC expects to reach much higher efficiencies with added surface passivation and texturing.

Tell Us What You Think

Do you have a review, update or anything you would like to add to this news story?

Leave your feedback
Your comment type
Submit

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.